QL-705M PVDC lotion

is a high solid content of polymer waterborne resin dispersion, the use of a small amount of film forming additives and wetting agent mixed evenly reserved, in the metal surface anti-corrosion pretreatment after coating PVDC emulsion; After natural drying, multi-channel coating, so that the thickness of the paint film is greater than 70um, and its salt spray resistance can reach more than 500 hours; It has the advantages of fast film formation, low VOC content, good adhesion to metal substrates, good paint film strength, etc., and can be used for metal anti-corrosion treatment such as steel structures, pipelines, storage tanks, bridges, metal brackets, auto parts and so on.

Keywords：

Coating

Subclassification：

Hotline：

QL-705M PVDC lotion

Product use: is a high solid content of polymer waterborne resin dispersion, the use of a small amount of film forming additives and wetting agent mixed evenly reserved, in the metal surface anti-corrosion pretreatment after coating PVDC emulsion; After natural drying, multi-channel coating, so that the thickness of the paint film is greater than 70um, and its salt spray resistance can reach more than 500 hours; It has the advantages of fast film formation, low VOC content, good adhesion to metal substrates, good paint film strength, etc., and can be used for metal anti-corrosion treatment such as steel structures, pipelines, storage tanks, bridges, metal brackets, auto parts and so on.

Product application processing & drying requirements: applicable coating technologies include brushing, rolling, spraying, etc. When priming metal, the surface pretreatment must be treated well, and the surface must be dry after each coating. After coating, it needs to be cured at 35°C for one day or room temperature for 10 days.

Packaging, storage and transportation: light loading and unloading should be carried out during transportation to prevent collision and avoid rain, exposure and pollution. The product should be stored in a ventilated, dry, cool and clean warehouse, and heavy pressure is strictly prohibited.

Packing specifications: 250kg, 1200kg;

project	unit	index
Emulsion type	/	anion
appearance	-	milky
Solid content	%	55±1
density	kg/dm³	1.27-1.29
surface tension	mN/m	>45
PH	/	1-2
viscosity	cps	15-80
Minimum film-forming temperature	℃	12-17
Surface dry (25°C)	Min	25-35
adhesion		Level 1
Resistant to salt spray	H